s****y
发帖数: 62 | 1 菜鸟最近在读一些有关RAMAN 的文章， 尤其是SERS。
很多文章，在用 ELISA 和 SERS 联合起来检测antigen。
基本思路是，gold的nano particles上面加上antibody和raman reporter， 然后bond
想要检测的
antigen，然后用SERS 检测。
有1个疑问，想请教大家。
SERS的原理是纳米级的颗粒因为表面粗糙，所以会增强raman的信号。
既然这样，为什么要在gold nanoparticles上面链接raman reporter?
谢谢各位。 |
|
l******u
发帖数: 2314 | 2 【Full Text链接请访问：
http://nanotofu.blogspot.com/2007/09/raman-spectroscopy-of-swnts.html】
【按：应xiaoyi2008要求，这里收录的是对搞碳管化学的同志们相当有用的部分SWNT
Raman文章。收录当然远非完整，但是足够大家了解SWNT Raman的概念和用途。我自己
会继续更新，也欢迎大家补充。】
Discovery - RBM:
Rao, A. M.; Richter, E.; Bandow, S.; Chase, B.; Eklund, P. C.; Williams, K.
A.; Fang, S.; Subbaswamy, K. R.; Menon, M.; Thess, A.; Smalley, R. E.;
Dresselhaus, G.; Dresselhaus, M. S.
Diameter-Selective Raman Scattering from Vibrational Modes in Carbon
Nanotubes. Science 1997, 275, 187.
R |
|
d*****c
发帖数: 59 | 3 For CNT thin film characterization, would FT-Raman be useful?
Or do we have to use Dispersive Raman? (For thin films, we have
to use microscope to help focusing)
We have been using other's dispersive raman,the excitaion laser is 785nm.
Now, we are thinking to upgrade our FT-IR system into raman range.
Just wondering if there is any chance we can do that?
Any response will be appreciated.
(sorry i can't type in chinese here) |
|
M*V
发帖数: 3205 | 4 http://en.wikipedia.org/wiki/Raman_spectroscopy
http://en.wikipedia.org/wiki/Sir_C._V._Raman
The Raman effect was named after one of its discoverers, the Indian
scientist Sir Chandrasekhara Venkata Rāman who observed the effect by means
of sunlight (1928, together with K. S. Krishnan and independently by
Grigory Landsberg and Leonid Mandelstam).
Raman won the Nobel Prize in Physics in 1930 for this discovery accomplished
using sunlight, a narrow band photographic filter to create monochromatic
l... 阅读全帖 |
|
y*********n
发帖数: 40 | 5 【 以下文字转载自 Chemistry 讨论区 】
发信人: yijijuechen (yijijuechen), 信区: Chemistry
标 题: a question about Raman, Thanks
发信站: BBS 未名空间站 (Thu Feb 12 21:21:29 2009)
I am a beginner in Raman. I got a peak at 3500 on doped BaCeO3 (a proton
conductor). Does Raman make a difference between surface water molecules and
OH bond in the bulk materials? Thanks for your help |
|
o**t
发帖数: 55 | 6 最近需要用到Raman光谱,可是没有什么基础
请教:
有什么关于Raman的书比较好,求推荐.
请教如何分析Raman光谱,有什么比较好的软件没?
谢谢 |
|
s****y
发帖数: 62 | 7
另外，如果加上了reporter, raman测出来的是reporter的信号，那怎么能判断是
antigen呢？
这些问题比较肤浅，希望不要见笑。我一直做GCMS 没了解过raman。
谢谢你的解答。 |
|
b*******g
发帖数: 1309 | 8 你是缺乏sandwich assay 的常识
不管是用 raman，还是很Fluorescence，还是其他的
基本原理都是用antibody 识别analyte，然后 antibody 本身连一个信号reporter（或
者上第二个antibody，上面连reporter），
可以是这里的raman，也可以是酶催化的荧光，还可以是ECL，等等
因为antibody 跟antigen 是特异性结合，所以有antigen在，才有antibody，有
antibody 就有reporter的信号，而且这个信号说不准还是放大了几千几万倍，这样灵
敏度才高。 |
|
s****y
发帖数: 62 | 9
一个问题是，raman 给出来的是function group的图谱，GCMS那种给出来的是保留时间
和碎片。
如果是raman的话，给出来的是reporter的信号，那从图谱上没办法判断是antigen的
function
group。
说的比较混乱，不知道这位专家能不能解答一下这个问题。
谢谢各位的帮忙了。 |
|
s****y
发帖数: 62 | 10 请假大家一个问题
SERS用Au做substrate是利用nano金表面粗糙分布来增强信号。
所以它的顺序是 金的地盘，上面有target analyte。化合物是放在金的上面。
在2010年厦大一个教授发表在nature上面一个文章，叫shell isolate nanoparticle
enhanced Raman spectroscopy.
他们做的是一种金的nano颗粒，然后撒在表面，用来增强Raman信号。我想请教一下，
这个方法，金颗粒是撒在化合物的上面还是在下面？如果是在化合物的上面，那他是利
用什么原理增强信号的？
这个是nature上面的那个文章的link ：
http://www.nature.com/nature/journal/v464/n7287/full/nature0890
有兴趣的同学可以看一下~做Raman的专家也请大概看一下，然后帮忙解释一下，可以吗？
谢谢各位的帮忙。 |
|
x*******i
发帖数: 32 | 11 You are using a home-made Raman instrument right? For confocal Raman
instruments from major vendors, you do not need to consider how to measure
the distance of the focus movement, because it is controlled by stage with
spatial resolution of 100 nm (normal type) or 10 nm (advanced type).
I need some time to think about how to answer your question. But confocal
Raman experiment may not be able to determine the thickness by the technique
itself on the well-known sample, because the refractive index... 阅读全帖 |
|
l******u
发帖数: 2314 | 12 [http://nanotofu.blogspot.com/2007/10/everything-you-need-to-know-about-cnt.html]
Raman Spectroscopy of Carbon Nanotubes in 1997 and 2007
M. S. Dresselhaus, G. Dresselhaus, and A. Jorio
Journal of Physical Chemistry C
Web Release Date: 02-Oct-2007; (Article) DOI: 10.1021/jp071378n
Abstract Full: HTML / PDF (185K)
【简评】就在我辛辛苦苦地拼接了《豆腐文摘特辑：Raman Spectroscopy of SWNTs》而“元气大伤”之后的不到一个星期，Dresselhaus老人家夫妇和Jorio博士三人便在JPCC上登出了这篇简明扼要的CNT Raman十年综述，作为纪念Richard E. Smalley特刊的一部分。
前面有同学抱怨我的文摘里收录的文章部头太大，OK - Dre |
|
w********o
发帖数: 10088 | 13 老看见大家测raman谱，出来的peak都是用raman shift表示的，单位是1/cm
这个raman shift怎么和phonon energy联系起来呢？比如说我知道这个shift的value,
想算对应phonon energy该怎么算呢？
谢谢 |
|
F********E
发帖数: 1025 | 14 I found lots of papers about the difference spectra of rhodopsin or
bacterhodopsin, but didn't find the original vibrational spectra (IR Raman
or THz). Could somebody help me or give some hints to find the the original
vibrational spectra (IR Raman or THz) of rhodopsin or bacterhodopsin? Thanks
a lot! |
|
r*******6
发帖数: 545 | 15 要做一点Raman光谱的实验，不知哪个Raman光谱数据库比较全？有没有免费的？
谢谢1 |
|
|
f**p
发帖数: 792 | 17 那是测的东西本身的raman, 你现在需要的是测两个东西的结合，用reporter可
能更好操作 |
|
v*****s
发帖数: 20290 | 18 antigen的Raman信号一般比较复杂，峰比较多，不同的antigen也不好区分。通过
antibody bond以后，把Au NP固定住，再通过reporter就可以准确定位了。这个一般是
做imaging的，需要有某种手段把没固定住的Au NP弄掉，防止干扰。另外一个原因是
reporter一般是dye，比antigen的信号要强几个数量级。
你可以具体说一下哪篇paper，大家一起讨论看看。 |
|
s****y
发帖数: 62 | 19
Anal. Chem. 2010, 82, 5290–5295
On-Chip Immunoassay Using Surface-Enhanced
Raman Scattering of Hollow Gold Nanospheres |
|
b*******g
发帖数: 1309 | 20 GC-MS or any MS 是直接检测analyte 的信号
你上面提到的是间接检测，不是直接检测antigen的raman 信号，而是间接检测
reporter 信号，然后这个信号强度是跟antigen的浓度相关的
其中antibody 的存在，保证了reporter的信号是跟antigen有关
好好看看这个ELISA 的wiki
http://en.wikipedia.org/wiki/ELISA
另外所有的 immuno assay 大致都是这个原理，跟你想像的直接检测不一样 |
|
s****y
发帖数: 62 | 21
谢谢你，明白了。是根据2个比较出来的
一个图是raman reporter 没有任何sandwich complexes连上面的信号
一个是有sandwich complexes链接上面的信号。
比较第二个信号比第一个信号减弱多少来判断出来多少antigen吸附在antibody上面
这个理解对不对。谢谢你的回复。 |
|
h***o
发帖数: 350 | 22 Laser power dependence of Raman scattering on YBa2Cu3O7−x thin films
N. T. Liang1,
W. S. Tse1,*,
M. C. Chang1,
H. T. Chen2,
T. T. Chen2
Journal of Raman Spectroscopy
Volume 24, Issue 3, pages 179–181, March 1993
Could you please send to s**************[email protected]?
Thank you very much. |
|
h***o
发帖数: 350 | 23 Journal of Raman Spectroscopy
Volume 7, Issue 6, pages 321–324, December 1978
Raman spectrum of anatase, TiO2
Toshiaki Ohsaka, Fujio Izumi, Yoshinori Fujiki
Thank you very much! |
|
h***o
发帖数: 350 | 24 Journal of Raman Spectroscopy
Volume 26, Issue 1, pages 57–62, January 1995
The Raman spectrum of brookite, TiO2 (Pbca, Z = 8)
G. A. Tompsett,
G. A. Bowmaker,
R. P. Cooney*,
J. B. Metson,
K. A. Rodgers,
J. M. Seakins
Thank you very much! |
|
w*n
发帖数: 34 | 25 We have a system for bulk fluoresce and Raman. Is it possible to
make it do thin film Raman? What kind of adjustment we have to
make? We have tried for some time, no luck so far.
The main prolems is that we cannot get sufficient signal from the
film. We are getting all signal from the substrate.
Thanks! |
|
s*********d
发帖数: 13 | 26 你的激光波长多少？x轴换成raman位移
也许我孤陋寡闻了，头一次见到raman谱用波长做横坐标的
俺用的几种激光，硅的信号在300和520cm-1
最后还要感叹一声，真牛的拉曼，俺们这的到不了那么高波长 |
|
l******u
发帖数: 2314 | 27 也不知道翻译的对不对。
今天看到Hongjie Dai组的JACS的ASAP: "Multiplexed Multicolor Raman Imaging of
Living Cells with Isotopically Modified SWNTs"。见附件。今年春天ACS和这位
Zhuang Liu兄弟有幸有一面之缘。
最后有多大用不谈，单单从science角度讲，抛开SWNT不谈，如果这是第一次用C12/C13
的G-band shift做Raman Imaging的话，真是灰常creative、灰常amazing了。大家看看
吧。 |
|
y********4
发帖数: 1116 | 28 我主要用AFM和RAMAN测量graphene，我们并不需要极高的resolution，因为我们主要做
器件而不是机理研究。请问什么档次的AFM或是RAMAN比较适合我们。什么类型的激光器
？AFM的resolution大概在多少？谢谢 |
|
A***N
发帖数: 219 | 29 大概有五，六千刀的预算， 能买到像样的Raman Microscope吗？（刚更新了一下，不要连带知谱
仪的）。
样品主要是多壁碳管。有经验的朋友请给点建议。
另外，哪家公司的仪器比较好用？ 比如说结果便于整理之类的。
我知道的有 Thermo Scientific DXR Raman Microscope 和 Jobin Yvon LabRam HR800
。版上如
果有用过这两家仪器的朋友，请给点评价吧。 |
|
E*******1
发帖数: 3464 | 30 你说你怎么学的，这个出来的当然不是声子的wave number，是前后inelastic light
scattering的能量差，说白了是光子的wave number， 你把能量守恒和动量守恒混成一
个方程了
Raman里面声子的q理论上只能是0啊，因为声子的波数和光子的波数差了好几个量级，
否则为什么1st order raman只能记录gamma点上的信息
不能用光的速度吧？只知道波长，不知道频率，不是还是算不出来能量么
知道有效质量。这个phonon的质量一般怎么取呢？ |
|
E*******1
发帖数: 3464 | 31 c*h/lamda_1-c*h/lamda_2==Delta_E_light=c*h/RamanShift
Delta_E_light==E_phonon
里面不涉及任何有关声子的wavenumber啊，因为raman是用光子probing的，你要算声子
的wavenumber得知道声子的色散关系，比如用简单的德拜模型 E_phonon==h*v*q，声速
v才千米/s量级，所以声子的波矢在raman谱中只有q=0
关系 |
|
s********3
发帖数: 231 | 32 物理化学专业，有文章18篇，
10分以上一作2片，3~7分一作3片。
引用约350次。现严重缺审稿。希望好心人帮忙推荐一下审稿，站
内联系！我会发简历，非常感谢！
领域：Nanoscience and Nanotechnology,nano-optics, single molecule
spectroscopy,electrochemistry,Raman spectroscopy,fluorescence spectroscopy. |
|
s*****n
发帖数: 39 | 33 Surface enhanced Raman, Photoactive Yellow Protein, Modification/Reaction
请将姓名，工作单位，邮箱，以及一小段相关研究介绍，相关论文站内给我。 |
|
d*******n
发帖数: 1566 | 34 有没有人读过这篇paper！
http://prb.aps.org/abstract/PRB/v58/i19/p12899_1
Phys. Rev. B 58, 12899–12907 (1998)
Phonon dispersion and Raman scattering in hexagonal GaN and AlN
Abstract
References
Citing Articles (122)
Download: PDF (182 kB) Buy this article Export: BibTeX or EndNote (RIS)
V. Yu. Davydov*, Yu. E. Kitaev, I. N. Goncharuk, and A. N. Smirnov
Ioffe Physical Technical Institute, St. Petersburg 194021, Russia
J. Graul, O. Semchinova, and D. Uffmann
LFI Universitat Hannover, Schneiderberg 32, 30167 |
|
e*****1
发帖数: 892 | 35 AgNO3和柠檬酸三钠还原得Ag nanoparticles,这是经典方法。但我怎么发现只是Ag
nanoparticles 在干净的cover glass上也有类似Raman的peaks.而且很强（我在700－
1800cm-1之间收集拉曼信号。重复实验多次，starting material没问题，都是sigma的
，99％以
上。) 文献中没有见过这种现象，奇怪。 |
|
h*******o
发帖数: 1114 | 36 有人做过3D Raman效果图吗？我用Grams AI做出来了，但是怎么都没法编辑，请教一下
，麻烦告诉怎么做，谢谢！ |
|
|
S*********h
发帖数: 61 | 38 Based on some literatures, the Raman peak width is related to crystal
structure. But what is the theory basis for this? any body have any ideas
about this? thank you very much.
If you know some big niu guy, please let me know .
Thanks |
|
s**********x
发帖数: 4593 | 39 我以前collaborate的一个组做过Raman peak width 对semiconductor device的研究,
加越大的bias，或者heat更高的温度，FWHM就越宽，
如果你要的话我可以帮你找找那片paper |
|
z***3
发帖数: 496 | 40 请教一下关于raman的depth profiling
实验室用的是共焦显微拉曼，想给样品做depth profiling（深度剖析）。就是把焦点
放在样品不同的厚度上，然后比较各样品层的谱图。
一般是通过调节显微镜的上下移动旋钮去调节焦点，虽然旋钮上有刻度， 可问题是
怎么才能知道，旋几格刻度就是焦点移动了2微米，旋几格刻度就是焦点移动了5微米
呢？ 有什么实验可以验证呢？
非常感谢
（不好意思，已经修改，应该是微米） |
|
x*******i
发帖数: 32 | 41 Then there is no need for you to worry about movement of the focus. You can
control the focus movement of the stage using software. If you are using oil
immersion objective or water immersion/dipping objective, the stage
movement is equal to the focus movement. Otherwise if you are using a dry
objective, the stage movement is smaller than the real thickness roughly by
a factor of refractive index. One of the first papers to discuss this
artifact is Applied spectroscopy 2000, 54, 773. I remember ... 阅读全帖 |
|
z****r
发帖数: 330 | 42 老板最近有提到关于COOH基团的Raman tag（不知道有没拼错），是用于增强样品表面
信号的。 就是那种加入金属银的surface enhance么
thx |
|
g*****y
发帖数: 10 | 43 As far as I know, it is ipossible for you to measure the Raman signal
by using your system. Your system does not have such function for thin film.
The signal from the thin film is very weak. you can get the signal of the
substrate, however, the signal is not enough for detecting in such system. |
|
f**********e
发帖数: 16 | 44 CNT： carbon nanotube
PP: polypropylene
PP的信号是不是会被CNF的掩盖掉，想测这两种component的orientation. 对Raman不太懂
得说。 |
|
f********e
发帖数: 40 | 45 Dresselhaus组2005有一篇关于碳管Raman的综述，算是比较全面的。
. |
|
s**l
发帖数: 869 | 46 single wall tube
应该是在硅片上看得
左边1170左右的小峰是硅的吗？谢谢
但我搜了一下si的raman峰，说是300左右？？ |
|
|
|
l******u
发帖数: 2314 | 49 不是同位素的问题，是同位素的拉曼峰位移做multiplex imaging的问题。
Raman imaging“不新”，碳同位素的拉曼峰位移也“不新”，但是能想到把两个合在
一起就不仅仅是“换一个probe而已”吧。
要是那么说的话，没有任何科学可以被归类到“很新”的那一类了，呵呵 |
|
t***s
发帖数: 163 | 50 you may think about wavelength of laser for Raman. |
|