c****e
发帖数: 1628 | 1 注意这段话"Current evidence from archaeology indicates that cast iron was
first produced in Europe at two sites in Sweden, Lapphyttan and Vinarhyttan,
sometime between 1150 and 1350"并且有可能是蒙古人从中国带过去的。
中国汉代就知道把生铁和“熟铁”合炼，调节铁碳含量而成钢。也就是所谓的“灌钢”。
在欧洲，直到17世纪才认识到这一点。
Medieval Iron and Steel -- Simplified
Bert Hall
Institute for the History and Philosophy of Science and Technology
University of Toronto
----------------------------------------------------------------------------
----
Iron is one of the most useful metals ever discovered, but it is also one of
the more difficult metals to understand in history, especially in medieval
history. Iron comes in several forms, and the complications involved in
producing each of them fosters further confusion. What follows is the layman
's guide to medieval iron -- as simple as possible, but not one bit more!
----------------------------------------------------------------------------
----
Three Forms of Iron:
Pure, unadulterated iron is only moderately hard, as anyone who has bent a
nail with a hammer can attest. When it becomes red hot, say at about 700
degrees Celsius, it can be easily bent and formed into whatever shape the
artisan wishes -- straps, hinges, horseshoes. For this reason we speak of "
wrought iron," (wrought, from wreak, to bend or twist). Unfortunately, it is
also only moderately tough; it can easily be bent when being used. It also
loses any sharp edge very quickly under the pressure of work or abrasion.
Cast iron, on the other hand, is enormously strong. Cast iron takes its name
from the fact that it emerges from the smelter in liquid form (see below)
and can be cast into moulds rather like bronze or silver. Unfortunately, it
is rather brittle, and worse, it can't be bent or shaped in any way once it
has solidified. Hammering on red hot, even white hot, cast iron will simply
break it.
Steel, iron with a small amount of carbon dissolved inside its structure,
combines the best of both worlds. It can be cast into moulds from the
furnace, shaped when red hot, and it holds an edge when it has been
sharpened, even under fairly heavy use. Steel is clearly the prince of
ferric metals, but it's not easy to make.
Carbon is the major variable that distinguishes between wrought iron, steel,
and cast iron. Too little, and one gets wrought iron; too much and the iron
begins to flow as cast iron. Just the right amount of carbon (around 1% or
a bit more) and you've got steel. So why didn't everyone make steel? Because
the smelting furnace doesn't let the operator control the carbon content
with any degree of precision.
----------------------------------------------------------------------------
----
What Happens in the Smelting Furnace?
The job of the smelting furnace is to reduce the metal from its chemically
combined state to a metallic state. Iron is a reasonably common substance in
the earth, but as any owner of an old car will attest, most of the time it
takes the form of rust, iron oxide. In the smelter, iron oxides and other
chemically combined forms of iron have their chemical bonds broken. This
allows the iron atoms to combine into a mass of metal. Rust goes in; iron
comes out.
The smelting furnace has two tools to bring about this transformation: heat
and carbon. Smelters, like all furnaces, burn carbon fuels to produce heat;
that much is obvious. But burning is never complete, and the hot gases
within a smelter are rich in carbon that is chemically active. Hot carbon
has a strong affinity for oxygen, and the oxygen atoms are literally
stripped away from the iron by the gaseous carbon. Left without any chemical
partners, the iron atoms form a mass of nearly pure metal.
----------------------------------------------------------------------------
----
Heat and the Forms of Iron
The temperature inside the furnace is a critical variable. Most early
smelters in Europe could no reach average temperatures of about 700 degrees.
Now pure iron has a very high melting point, about 1530 degrees. So when
the newly-formed mass of iron coalesces at 700 degrees, it remains a red-hot
, slightly plastic solid called a bloom. The smith can hammer on this hot
mass to shape it (and to make it extrude lumps of impurities that it might
otherwise congeal around).
The bloomery type of smelter must produce wrought iron. No carbon can
dissolve in the iron bloom at 700 degrees. But what happens if we start
raising the temperature inside the carbon-rich conditions of the smelter?
Simplistically, we would expect to have to get to about 1500 degrees before
the bloom would start to melt. But this isn't the case at all.
At much lower temperatures, around 1150-1200 degrees, the iron starts to
flow as a liquid. What has happened is one of the great "tricks" of physics
-- a so-called eutectic point. When the temperature in a smelter rises, more
and more carbon is absorbed by the iron. At about 3.5% carbon content, the
iron-carbon alloy has a melting point much lower than either element would
have by itself. It liquifies and begins to try to flow out of the furnace.
Iron has an extremely strong tendency to behave this way. The energy in its
chemical bonds is such that the iron will absorb free carbon up to the 3.5%
mark very quickly once the right temperature is reached, and the iron
liquifies itself in the process. There is simply no way to stop the process
once it starts, and that is why no master smith can realistically expect to
make steel in a smelter.
What you get out of a smelting furnace depends on the amount of heat it
generates. At lower temperatures, the iron is reduced without ever becoming
liquid; it is drawn out as a spongy solid, red-hot and malleable, with
virtually no carbon in its crystalline structure. At higher temperatures,
the iron flows from the furnace into moulds, but it is virtually saturated
with carbon and it cannot be shaped any further after it has cooled and been
removed from its mould.
----------------------------------------------------------------------------
----
Making Steel
Both wrought iron and cast iron have their uses, but since neither form of
iron has ideal properties, the smith will probably want to make steel, at
least in small amounts. To do this, he needs another type of furnace. If he
is faced with high-carbon cast iron, he must use an oxygen-rich furnace to
try to "decarburize" or reduce the carbon content. If he is faced with low-
carbon wrought iron, he must somehow produce a carbon-rich environment that
would encourage limited amounts of carbon to combine with the iron.
Both tasks are hard to control in practice, but there is evidence that both
methods were practiced in different parts of the world. Western smiths
usually followed a process of heating the low-carbon wrought iron in some
type of sealed container containing carbon, the idea being to promote the
migration of carbon atoms into the metal. It was tricky, and often produced
only small amounts of steel, but steel was simply so useful for tools and
weapons that even small amounts were important. Steel edges were usually
welded to a wrought iron core or blade to make a steeled tool in the most
economical manner.
----------------------------------------------------------------------------
----
Some History
Broadly speaking, Europeans were devoted to the bloomery process until late
in the Middle Ages, while the Chinese followed the opposite path, producing
high-quality iron castings from the Chou Dynasty onward. The Chinese made
steel or wrought iron by decarburizing their high-carbon cast iron, while
Europeans made steel from their low-carbon wrought iron and seem not to have
used cast iron at all. (There is some evidence the Romans made small
amounts of cast iron by accident and discarded it as a "waste product.")
Throughout the European Middle Ages there is a great deal of iron in use.
There are many centers of production, and a great deal of experiment in
changing technique. One constant theme is the application of water-power to
the "muscle jobs" of hammering the bloom and blowing air onto the smelter
fire. The larger bellows that a water-wheel can operate mean a hotter fire
in the smelter, and along with changes in the size and shape of the furnaces
, they make it possible to reach the critical temperatures.
Current evidence from archaeology indicates that cast iron was first
produced in Europe at two sites in Sweden, Lapphyttan and Vinarhyttan,
sometime between 1150 and 1350. This suggests a possible connection with the
much earlier Chinese practice of iron casting perhaps via the Mongols and
the "Viking" settlements in the Volga region. This suggestion is supported
by the general shapes of the furnaces as well. On the other hand, it may
simply have been that bigger furnaces and bigger bellows led inevitably to
cast iron flowing from the smelters.
One mystery remains: even if Europeans were making cast iron is Sweden by
the thirteenth century, they weren't using it as iron castings. We have no
pots or pans or bells or firebacks from such an early a date. Most likely
the Swedish smiths were decarburizing the product of their smelters to make
common wrought iron. Indeed, it is even possible that their effort failed
and their knowledge lost for a time.
The market for cast iron objects in Europe appears late in the fourteenth
century when cannonballs came to be in demand. Iron casting could make cheap
, uniform cannon shot in vast quantities, and with this as a base, iron
masters learned to produce and sell other simple objects for household use.
Smiths also became skilled at making different forms of steel from cast iron
, objects of high value when made into weapons.
In time, they would learn to make cannons as well as cannonballs out of cast
iron, but the bulk of the smelter's output was destined to be converted
into wrought iron, the familiar and easily-worked form of iron on the
European market. It wasn't until the mid-nineteenth century that Henry
Bessemer learned how to make steel in vast quantities and at prices that
could compete with wrought iron. |
|