s*********s
发帖数: 18 | 1 为什么理论预测graphene spin diffusion length 可达到100 um,但实际测量还不到
10um, 室温只有1-2 um 在single layer graphene. 另外：Spin life time is 50-
200ps, the order of magnitude shorter than expected from the intrinsic spin-
orbit coupling(-us).The results indicates that the presence of the extrinsic
spin relaxation mechanism.
请前辈指点。
why graphene for spintronics?
1. Extraordinary high mobility
>200000cm2v-1s-1 (suspended , low temperature)
>40000cm2v-1s-1 (on sio2 , room temperature)
-------Future high-speed transistor materials
2.only light atoms (carbon)-----small spin-orbit interaction
long spin relaxation time
high mobility ----long spin coherent length
----------------Future spintronics devices | g*******g
发帖数: 447 | 2 spintronics是什么？我觉得这个都还没有完全定义好。
graphene spintronics 只不过是很多graphene泡泡中的一个罢了
graphene 肯定会有用，但是十有八九是低端的低科技应用 | g*******g
发帖数: 447 | 3 再说你问的这个问题不是你自己已经回答了吗
轻原子导致自旋轨道耦合弱，所以spin relaxation时间长
mobility高，Fermi velocity高 所以spin relax之前可以
走的远 | s*********s
发帖数: 18 | 4 这个是理论方面的说法：
轻原子导致自旋轨道耦合弱，所以spin relaxation时间长
mobility高，Fermi velocity高 所以spin relax之前可以
走的远
但实际测量的值远没有达到理论预测值100um. | s*******i
发帖数: 12823 | 5 这个argument没考虑各种spin flip 的 disorder, dopants的贡献吧
【在 s*********s 的大作中提到】
: 这个是理论方面的说法：
: 轻原子导致自旋轨道耦合弱，所以spin relaxation时间长
: mobility高，Fermi velocity高 所以spin relax之前可以
: 走的远
: 但实际测量的值远没有达到理论预测值100um.
| s*****u
发帖数: 164 | 6 PRL 103, 026804 (2009)
这篇文章说，杂质原子跟碳原子的电子轨道杂化，可以导致
足够强的旋轨耦合。 | c**********9
发帖数: 33 | 7 Theoretical predictions:
curvature, localized magnetic moments, hydrogen doping, etc.
D. Huertas-Hernando, F. Guinea and A. Brataas, Eur. Phys. J. Spec. Top. 148
(2007), p. 177.
C. Ertler, S. Konschuh, M. Gmitra and J. Fabian, Phys. Rev. B 80 (2009), p.
041405(R).
A.H. Castro Neto and F. Guinea, Phys. Rev. Lett. 103 (2009), p. 026804.
D. Huertas-Hernando, F. Guinea and A. Brataas, Phys. Rev. Lett. 103 (2009),
p. 146801.
Other possible reasons: The short spin life is measured by Hanle effect.
This measurement maybe measures the lower limit of the spin lifetime.
BTW: the spin lifetime in graphene (SLG, BLG) can reach 0.77 ns in SLG at RT
, and 1.2 ns at 4 K. For BLG, the spin lifetime is ~ 6 ns at 20 K, and 2 ns
at RT.
Phys. Rev. Lett. 107, 047206 (2011)
Phys. Rev. Lett. 107, 047207 (2011)
spin-
extrinsic
【在 s*********s 的大作中提到】
: 为什么理论预测graphene spin diffusion length 可达到100 um,但实际测量还不到
: 10um, 室温只有1-2 um 在single layer graphene. 另外：Spin life time is 50-
: 200ps, the order of magnitude shorter than expected from the intrinsic spin-
: orbit coupling(-us).The results indicates that the presence of the extrinsic
: spin relaxation mechanism.
: 请前辈指点。
: why graphene for spintronics?
: 1. Extraordinary high mobility
: >200000cm2v-1s-1 (suspended , low temperature)
: >40000cm2v-1s-1 (on sio2 , room temperature)
|
|